Title: Synthesis of (Ti,Cr)C and (Ti,W)C solid solutions powders by mechanical alloying: Application for cutting tools

Mohsen Mhadhbi

Mohsen Mhadhbi has Ph.D. of Chemistry from the Faculty of Sciences of Sfax at University of Sfax (Tunisia). Since 2011, he is Assistant Professor and member of a research team of Laboratory of Useful Materials focusing on synthesis and characterization of nanomaterials for industrials responders (hydrogen storage, cutting tools and biomedical applications) at National Institute of Research and Physical-chemical Analysis at University of Carthage (Tunisia). Mhadhbi has served as teacher in Inorganic Chemistry in different Institutes in Tunisia. He has supervised several researchers in materials science. Her published work in national and international impacted journals and books. Mhadhbi is a member of different associations. He is also reviewer's and editorial board member in different scientific journals and congresses.


TiC- and Ti(CN)-based cermets have been used as cutting tool materials because of their attractive mechanical properties. In this work, solid solution nanocrystalline powders, (Ti,Cr)C and (Ti,W)C, were prepared by mechanical alloying (MA) from a mixture of elemental Ti, Cr, C and Ti, W, C powders, respectively. Mechanical alloying were carried out in a planetary ball mill (Fritsch pulverisette 7), at room temperature. The powders were MA for 20 hours under argon atmosphere. The MA powders were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The experimental results indicate the formation of nanocrystalline (Ti,Cr)C and (Ti,W)C solid solutions with a mean crystallite size of 20 and 15 nm, respectively. The short diffusion path and the presence of defects induced during milling accelerated the solid state reaction.